Publications

Background/Objectives: The design of alternative antipathogenic sprays has recently attracted much attention due to the limitations of existing formulations, such as toxicity and low and narrow efficacy. Polyethyleneimine (PEI) is a great antimicrobial polymer against a wide range of pathogens, but toxicity limits its use. Here, betainized PEI (B-PEI) was synthesized to decrease the toxicity of PEI and protonated with citric acid (CA), boric acid (BA), and HCl to improve antimicrobial activity. Methods: Cytotoxicity of the PEI-based solutions was determined on L929 fibroblast cells. Antibacterial/fungal activity of PEI-based antipathogenic sprays was investigated by microtiter and disc diffusion assays, in addition to bacterial viability and adhesion % of common bacteria and fungi on the PEI-treated masks. Furthermore, the antiviral effect of the PEI-based solutions was determined against SARS-CoV-2 virus. Results: The biosafe concentration of PEI was determined as 1 μg/mL with 75 ± 11% cell viability, but B-PEI and its protonated forms had great biocompatibility even at 1000 μg/mL with more than 85% viability. The antibacterial/fungal effect of non-toxic B-PEI was improved by protonation with BA and HCl with 2.5–10 mg/mL minimum bactericidal/fungicidal concentrations (MBCs/MFCs). Bacterial/fungal viability and adhesion on the mask was almost eliminated by using 50 μL with 5–10 mg/mL of B-PEI-BA. Both protonated bare and betainized PEI show potent antiviral activity against SARS-CoV-2 virus. Conclusions: The toxicity of PEI was overcome by using betainized forms of PEI (B-PEI). Furthermore, the antimicrobial and antiviral efficacy of PEI and B-PEI was improved by protonation with CA, BA, and HCl of amine groups on B-PEI. B-PEI-BA spray solution has great potential as an antipathogenic spray with broad-spectrum antimicrobial potency against harmful bacteria, fungi, and viruses without any toxicity.

Ut enim ad minim veniam, quis nostrud exercitation ullamco laboris nisi ut aliquip ex ea commodo consequat.

Glycerol (Gly) is a well-known, FDA-approved molecule posing three hydroxyl groups. Since Gly is biocompatible, here, it was aimed to prepare poly(Glycerol) (p(Gly)) particles directly for the first time for the delivery of therapeutic agents. Micrometer-sized particles of p(Gly) were successfully synthesized via the micro-emulsion method with an average size of 14.5 ± 5.6 µm. P(Gly) microparticles up to 1.0 g/mL concentrations were found biocompatible with 85 ± 1% cell viability against L929 fibroblasts. Moreover, p(Gly) microparticles were tested for hemocompatibility, and it was found that up to 1.0 mg/mL concentrations the particles were non-hemolytic with 0.4 ± 0.1% hemolysis ratios. In addition, the blood compatibility index values of the prepared p(Gly) particles were found as 95 ± 2%, indicating that these microparticles are both bio- and hemocompatible. Furthermore, Quercetin (QC) flavonoid, which possessed high antioxidant properties, was loaded into p(Gly) microparticles to demonstrate drug-carrying properties of the particles with improved bioavailability, non-toxicity, and high biocompatibility. The results of this study evidently revealed that p(Gly) particles can be directly prepared from a cost-effective and easily accessible glycerol molecule and the prepared particles exhibited good biocompatibility, hemocompatibility, and non-toxicity. Therefore, p(Gly) particles were found as promising vehicles for drug delivery systems in terms of their higher loading and release capability as well as for sustained long term release profiles.

Chondroitin sulfate (CS), a well-known glycosaminoglycan, was physically crosslinked with Fe(III), Gd(III), Zn(II), and Cu(II) ions to obtain CS-Fe(III), CS-Gd(III), CS-Zn(II), and CS-Cu(II) polymeric particles for multipurpose biological applications. The CS–metal ion-containing particles in the micrometer to a few hundred nanometer size range are injectable materials for intravenous administration. The CS–metal ion-containing particles are safe biomaterials for biological applications because of their perfect blood compatibility and no significant cytotoxicity on L929 fibroblast cells up to a 10 mg/mL concentration. Furthermore, CS-Zn(II) and CS-Cu(II) particles show excellent antibacterial susceptibility, with 2.5–5.0 mg/mL minimum inhibition concentration (MIC) values against Escherichia coli and Staphylococcus aureus. Moreover, the in vitro contrast enhancement abilities of aqueous CS–metal ion particle suspensions in magnetic resonance imaging (MRI) were determined by obtaining T1- and T2-weighted MR images using a 0.5 Tesla MRI scanner and by calculating the water proton relaxivities. Therefore, these CS-Fe(III), CS-Gd(III), CS-Zn(II), and CS-Cu(II) particles have significant potential as antibacterial additive materials and MRI contrast enhancement agents with less toxicity.

Glycol chitosan (GC) is a chitosan (CH) derivative with improved water solubility with regards to CH which affords significant solubility advantages. In this study, microgels of GC as p(GC) were synthesized by a microemulsion technique at various crosslinking ratios e.g., 5%, 10%, 50%, 75%, and 150% based on the repeating unit of GC using divinyl sulfone (DVS) as a crosslinker. The prepared p(GC) microgels were tested for blood compatibility and it was found that p(GC) microgels at 1.0 mg/mL concentration possessed a 1.15 ± 0.1% hemolysis ratio and 89 ± 5% blood clotting index value confirming their hemocompatibility. In addition, p(GC) microgels were found biocompatible with 75.5 ± 5% cell viability against L929 fibroblasts even at a 2.0 mg/mL concentration. By loading and releasing tannic acid (TA) (a polyphenolic compound with high antioxidant activity) as an active agent, p(GC) microgels’ possible drug delivery device application was examined. The TA loading amount of p(GC) microgels was determined as 323.89 mg/g, and TA releases from TA loaded microgels (TA@p(GC)) were found to be linear within 9 h and a total amount of TA released was determined as 42.56 ± 2 mg/g within 57 h. According to the Trolox equivalent antioxidant capacity (TEAC) test, 400 µL of the sample added to the ABTS+ solution inhibited 68.5 ± 1.7% of the radicals. On the other hand, the total phenol content (FC) test revealed that 2000 μg/mL of TA@p(GC) microgels resulted in 27.5 ± 9.5 mg/mL GA eq antioxidant properties.

Cyclodextrins (CDs) are natural cyclic oligosaccharides with a relatively hydrophobic cavity and a hydrophilic outer surface. In this study, alpha (α-), beta (β-) and gamma (γ-) CD particles were prepared by directly using α-, β-, and γ-CDs as monomeric units and divinyl sulfone (DVS) as a crosslinker in a single-step via reverse micelle microemulsion crosslinking technique. Particles of p(α-CD), p(β-CD), and p(γ-CD) were perfectly spherical in sub- 10 µm size ranges. The prepared p(CD) particles at 1.0 mg/mL concentrations were found biocompatible with > 95 % cell viability against L929 fibroblasts. Furthermore, p(α-CD) and p(β-CD) particles were found non-hemolytic with  2 % hemolysis ratios, whereas p(γ-CD) particles were found to be slightly hemolytic with its 2.1 ± 0.4 % hemolysis ratio at 1.0 mg/mL concentration. Furthermore, a toxic compound, Bisphenol A (BPA) and a highly antioxidant polyphenol, curcumin (CUR) complexation with α-, β-, and γ-CD molecules was investigated via Electrospray-Ion Mobility-Mass Spectrometry (ESI-IM-MS) and tandem mass spectrometry (MS/MS) analysis. It was determined that the most stable noncovalent complex was in the case of β-CD, but the complex stoichiometry was changed by the hydrophobic nature of the guest molecules. In addition, BPA and CUR were separately loaded into prepared p(CD) particles as active agents. The drug loading and release studies showed that p(CD) particles possess governable loading and releasing profiles.

Carboxymethyl chitosan (CMCh) is a unique polysaccharide with functional groups that can develop positive and negative charges due to the abundant numbers of amine and carboxylic acid groups. CMCh is widely used in different areas due to its excellent biocompatibility, biodegradability, water solubility, and chelating ability. CMCh microgels were synthesized in a microemulsion environment using divinyl sulfone (DVS) as a crosslinking agent. CMCh microgel with tailored size and zeta potential values were obtained in a single stem by crosslinking CMCh in a water-in-oil environment. The spherical microgel structure is confirmed by SEM analysis. The sizes of CMCh microgels varied from one micrometer to tens of micrometers. The isoelectric point of CMCh microgels was determined as pH 4.4. Biocompatibility of CMCh microgels was verified on L929 fibroblasts with 96.5 ± 1.5% cell viability at 1 mg/mL concentration. The drug-carrying abilities of CMCh microgels were evaluated by loading Vancomycin (Van) antibiotic as a model drug. Furthermore, the antibacterial activity efficiency of Van-loaded CMCh microgels (Van@CMCh) was investigated. The MIC values of the released drug from Van@CMCh microgels were found to be 68.6 and 7.95 µg/mL against E. coli and S. aureus, respectively, at 24 h contact time. Disk diffusion tests confirmed that Van@CMCh microgels, especially for Gram-positive (S. aureus) bacteria, revealed long-lasting inhibitory effects on bacteria growth up to 72 h.

Hyaluronic acid (HA) was crosslinked with Gd(III) and Fe(III) ions rendering physically crosslinked HA-metal(III) microgels as magnetic resonance imaging (MRI) enhancing contrast agents. These HA-Gd(III) and HA-Fe(III) microgels are injectable with size range, 50–5000 nm in water. The same isoelectric point, pH 1.2 ± 0.1, was measured for both microgels. HA-Gd(III) and HA-Fe(III) microgels are hemo-compatible biomaterials and can be safely used in intravascular applications up to 1000 μg/mL concentration. Furthermore, no significant toxicity was attained as 95 ± 8 and 81 ± 2% cell viability on L929 fibroblast cells at 100 μg/mL of HA-Gd(III) and HA-Fe(III) microgels were measured. Moreover, HA-Gd(III) microgels were found to afford significant contrast improvement capability in MRI with proton relaxivity, r1 = 2.11 mM−1 s−1, comparable with the values reported for Gd(III) labeled functionalized HA gel systems and commercial Gd based contrast agents.

Non-degradable, slightly degradable, and completely degradable micro/nanoparticles derived from chondroitin sulfate (CS) were synthesized through crosslinking reactions at 50%, 40%, and 20% mole ratios, respectively. The CS particles with a 20% crosslinking ratio show total degradation within 48 h, whereas 50% CS particles were highly stable for up to 240 h with only 7.0 ± 2.8% weight loss in physiological conditions (pH 7.4, 37 °C). Tobramycin and amikacin antibiotics were encapsulated into non-degradable CS particles with high loading at 250 g/mg for the treatment of corneal bacterial ulcers. The highest release capacity of 92 ± 2% was obtained for CS-Amikacin particles with sustainable and long-term release profiles. The antibacterial effects of CS particles loaded with 2.5 mg of antibiotic continued to render a prolonged release time of 240 h with 24 ± 2 mm inhibition zones against Pseudomonas aeruginosa. Furthermore, as a carrier, CS particles significantly improved the compatibility of the antibiotics even at high particle concentrations of 1000 g/mL with a minimum of 71 ± 7% fibroblast cell viability. In summary, the sustainable delivery of antibiotics and long-term treatment of bacterial keratitis were shown to be afforded by the design of tunable degradation ability of CS particles with improved biocompatibility for the encapsulated drugs.